PRODUCTS
Biodegradable + Thermal-Bonded
Nonwoven Fabric
"F+PCEL SHEET" is an eco-friendly, sustainable product that features 100% biodegradability, achieved by imparting thermal-bonding properties to cellulose nonwoven fabric.
Features of F+PCEL SHEET
-
- The cellulose nonwoven fabric used as the base material is made of plant-derived, eco-friendly materials, offering a soft texture, rapid water absorption, and excellent moisture retention properties.
-
- The thermal-bonding resin is biodegradable and coated on one side only, allowing for lamination processing without compromising the surface characteristics of the cellulose nonwoven fabric.
-
- "F+PCEL SHEET" biodegrades in about six months under typical soil environments, returning naturally to the earth.
[Biodegradability Evaluation]
(After 3 months)
Potential Fields & Application Examples
-
- Agricultural mulch sheets
-
- Seedling pots and packaging bags for gardening and home vegetable gardens
-
- Fruit protection bags (for pears, grapes, peaches, etc.)
-
- Ethical packaging bags for apparel (eco-friendly)
-
- Outer packaging bags for portable toilets, pet sheets, etc.
Compostable in home composting systems
- Outer packaging bags for portable toilets, pet sheets, etc.
[Example of Outer Packaging Application]
Water-Absorbing & Deodorizing Bag "F+BAG ACE"
Product Specifications
| Part Number (Product Code) | Basis Weight （g／㎡） |
Thickness （㎜） |
Bonding Strength (Sheet-to-Sheet) （N/15㎜） |
Product Size (mm Width × m Length) |
Notes (Supplementary Information) |
|---|---|---|---|---|---|
| FPS-5020 (Standard Product) |
70 | 0.3 | 7.4（150℃×5sec.） | 1,250×1,000 | Slitting, small rolls, etc., are available upon request. |
Product specifications are subject to change without prior notice.
Bonding Strength
| Conditions | 130°C × 5 sec. 0.1MPa |
140°C × 5 sec. 0.1MPa |
150°C × 5 sec. 0.1MPa |
|---|---|---|---|
| Bonding Strength （N/15㎜） |
4.4 | 6.8 | 7.4 |
Note: The above values are measured values and not guaranteed values.
Specimen: The resin-coated bonding surfaces of the nonwoven fabric sheets were laminated together under the specified temperature, time, and pressure.
Heat Sealing Conditions: Only the upper bar was heated to the specified temperature; the lower bar was fixed at 40°C.
Test Method: T-peel test, tensile speed: 300 mm/min., n=3.
Thermal lamination processing with various base materials can be handled by our group company,
Sankyo Giken Co., Ltd. Please feel free to contact us for consultation.